Pressure Pipe Comprising a Multimodal Polyethylene Composition With an Inorganic Filler

ABSTRACT

The present invention relates to a pipe or a supplementary pipe article comprising a polyethylene composition comprising a base resin which comprises (A) a first ethylene homopolymer fraction, and (B) a second ethylene homo- or copolymer fraction, wherein fraction (A) has a lower average molecular weight than fraction (B), and the composition further comprises (C) an inorganic mineral filler, wherein inorganic mineral filler (C) is present in the composition in an amount of 1 to 70 wt. %, and to the use of said composition for the production of a pipe or a supplementary pipe article.

The present invention relates to a pipe, in particular a pipe for the transport of pressurized fluids, comprising a polyethylene composition including a polyethylene base resin and an inorganic mineral filler. Furthermore, the present invention relates to the use of said composition for the production of a pipe.

Polyethylene compositions are frequently used for the production of pipes due to their favourable physical and chemical properties as e.g. mechanical strength, corrosion resistance and long-term stability. When considering that the fluids, such as tap water or natural gas, transported in a pipe often are pressurized and have varying temperatures, usually within a range of 0° C. to 50° C., it is obvious that the polyethylene composition used for pipes must meet demanding requirements.

In particular, it is a target for pipes for the transport of pressurized fluids (so-called pressure pipes) to withstand higher and higher (internal) design stresses, involving both a higher creep resistance and a higher stiffness. On the other hand, pressure pipes must also fulfil demanding requirements as to their rapid as well as slow crack propagation resistance, must have low brittleness and high impact strength. However, these properties are contrary to each other so that it is difficult to provide a composition for pipes which excels in all of these properties simultaneously. Furthermore, as polymer pipes generally are manufactured by extrusion, or, to a smaller extent, by injection moulding, the polyethylene composition also must have good processability. Finally, the polymer composition used for the pipe must also show good weldability because pipe systems are usually built up by welding or fusion, either as general jointing method between pipe system parts or jointing between layers, for example in multilayer pipe structures e.g. butt fusion, electro fusion, spin welding (friction welding) and hand or automated welding with additional welding materials. Thus, it is important that the composition used must show a certain minimum weld strength. It is known that especially for filled polymer compositions weld strength is usually poor.

It is known that in order to comply with the contrary requirements for a pipe material bimodal polyethylene compositions may be used. Such compositions are described e.g. in EP 0 739 937 and WO 02/102891. The bimodal polyethylene compositions described in these documents usually comprise a low molecular weight polyethylene fraction and a high molecular weight fraction of an ethylene copolymer comprising one or more alpha-olefin comonomers.

It is the object of the present invention to provide a pressure pipe comprising a polyethylene composition showing the above described combination of properties. In particular, it is the object of the invention to provide a pressure pipe comprising a polyethylene composition with an increased stiffness as compared to prior art materials and, at the same time, with sufficient rapid and slow crack propagation resistance, and impact strength, so that the demanding requirements for pressure pipes in these regards are fulfilled, and at least acceptable weldability.

The present invention is based on the surprising finding that the above mentioned objects can be achieved by a polyethylene composition comprising a multimodal, preferably bimodal, polyethylene base resin and an inorganic (mineral) filler. This finding is all the more surprising because it has hitherto been considered impossible that a polyethylene comprising a (mineral) filler would have sufficient rapid and slow crack resistance so that it can be used as a pressure pipe material.

Accordingly, the present invention provides a pipe or a supplementary pipe article comprising a polyethylene composition comprising a base resin which comprises

-   -   (A) a first ethylene homopolymer fraction, and     -   (B) a second ethylene homo- or copolymer fraction,         wherein fraction (A) has a lower average molecular weight than         fraction (B), and the composition further comprises     -   (C) an inorganic mineral filler,         wherein inorganic mineral filler (C) is present in the         composition in an amount of 1 to 70 wt. %.

It has been found that the pipes according to the invention have a significantly increased stiffness as shown by their flexural modulus while, simultaneously, have a high crack propagation resistance as concerns both rapid and slow crack propagation, and high impact strength. Furthermore, the composition used for the pipe of the invention also has good processability, comparatively low brittleness and good weldability.

It should be noted that the composition used for the pipes of the present invention is characterised not by any single one of the above defined features, but by their combination. By this unique combination of features it is possible to obtain pressure pipes of superior performance, particularly with regard to minimum required strength (MRS).

The term molecular weight where used herein denotes the weight average molecular weight M_(w). This property may either be used directly, or the melt flow rate (MFR) may be used as a measure for it.

The term “base resin” denotes the entirety of polymeric components in the polyethylene composition according to the invention. Preferably, the base resin is consisting of fractions (A) and (B), optionally further comprising a prepolymer fraction in an amount of up to 20 wt %, preferably up to 10 wt %, more preferably up to 5 wt % of the total base resin.

In addition to the base resin and the inorganic filler (C), usual additives for utilization with polyolefins, such as pigments (for example carbon black), stabilizers (antioxidant agents), antacids and/or anti-UVs, antistatic agents and utilization agents (such as processing aid agents) may be present in the polyethylene composition. Preferably, the amount of these additives is 10 wt % or below, further preferred 8 wt % or below, of the total composition.

Preferably, the composition comprises carbon black in an amount of 8 wt % or below, further preferred of 1 to 4 wt %, of the total composition.

Further preferred, the amount of additives different from carbon black is 1 wt % or less, more preferably 0.5 wt % or less.

Where herein the term “pipe” is used it is meant to comprise pipes as well as all supplementary parts for pipes such as fittings, valves, chambers and all other parts which are commonly necessary for a piping system.

Usually, a polyethylene composition comprising at least two polyethylene fractions, which have been produced under different polymerisation conditions resulting in different (weight average) molecular weights for the fractions, is referred to as “multimodal”. The prefix “multi” relates to the number of different polymer fractions the composition is consisting of. Thus, for example, a composition consisting of two fractions only is called “bimodal”.

The form of the molecular weight distribution curve, i.e. the appearance of the graph of the polymer weight fraction as function of its molecular weight, of such a multimodal polyethylene will show two or more maxima or at least be distinctly broadened in comparison with the curves for the individual fractions.

For example, if a polymer is produced in a sequential multistage process, utilising reactors coupled in series and using different conditions in each reactor, the polymer fractions produced in the different reactors will each have their own molecular weight distribution and weight average molecular weight. When the molecular weight distribution curve of such a polymer is recorded, the individual curves from these fractions are superimposed into the molecular weight distribution curve for the total resulting polymer product, usually yielding a curve with two or more distinct maxima.

In a preferred embodiment of the pipe of the invention, the composition has a MFR₅ of 0.1 to 2.0 g/10 min, more preferably of 0.2 to 1.5 g/10 min, still more preferably of 0.3 to 1.3 g/10 min, and most preferably of 0.4 to 1.0 g/10 min.

Further preferred, the composition has a MFR₂₁ of 2 to 50 g/10 min, more preferably of 5 to 30 g/10 min, and most preferably of 6 to 20 g/10 min. The flow rate ratio FRR_(21/5) of the composition which is indicative for the broadness of the molecular weight distribution of a polymer preferably is from 15 to 60, more preferably from 30 to 50.

With the pipe according to the invention, it is inter alia especially the stiffness of the composition which is dramatically improved thus enabling the production of pipes with significantly increased minimum required strength (MRS).

Accordingly, the composition used for the pipe according to the invention preferably has a flexural modulus determined according to ISO 178 of more than 1400 MPa, more preferably of more than 1600 MPa, still more preferably of more than 1800 MPa and most preferably of more than 2000 MPa.

Usually, the composition has a flexural modulus of 3000 MPa or below.

Furthermore, the flexural modulus of the base resin preferably is 1000 MPa or more, more preferably of 1200 MPa or more, still more preferably of 1300 MPa or more, and most preferably of 1400 MPa or more.

As mentioned, the pipe of the invention has a crack propagation resistance which is comparable to or even better than that of a pipe without an inorganic mineral filler.

Thus, the composition used for the pipe has a critical temperature T_(c) in the EN 13477 test for determining the rapid crack propagation of −1° C. or less, more preferably of −3° C. or less, still more preferably of −5° C. or less, still more preferably of −7° C. or less, and most preferably of −10° C. or less.

Furthermore, the composition preferably has a slow crack propagation resistance of at least 50 h at 4.6 MPa hoop stress and 9.2 bar internal pressure at 80° C. measured according to EN 13479, more preferably of 165 h, still more preferably of at least 500 h, and most preferably at least 1000 h.

It is preferred that a pipe made from the composition according to the invention has a time to failure in the Constant Tensile Load (CTL) test of at least 25 h, more preferably at least 30 h and most preferably at least 35 h.

Furthermore, it is preferred that the composition has at least only a slightly reduced time to failure in the CTL test of at most 5 h less than the basic polymer matrix, i.e. the matrix without the inorganic filler (C), more preferably has at least the same or a better time to failure in the CTL test than the basic polymer matrix, i.e. the matrix without the inorganic filler (C).

Still further, the impact resistance of the pipes of the invention is improved or at least not negatively affected by the incorporation of the inorganic filler.

The composition thus preferably has a Charpy Impact Strength at 23° C. of more than 20 kJ/m², more preferably of more than 40 kJ/m². Usually, the Charpy Impact Strength at 23° C. is 100 kJ/m² or below.

Furthermore, the composition preferably has a Charpy Impact Strength at 0° C. of more than 10 kJ/m², more preferably of 25 kJ/m². Usually, the Charpy Impact Strength at 0° C. is 80 kJ/m² or below.

Still further, the composition preferably has a creep resistance measured according to EN ISO 9967 as the creep ratio E(1 hour)/E(2 years) of 4.5 or below, more preferably 4.0 ore below, still more preferably 3.7 or below and most preferably 3.5 or below.

The composition preferably has a creep resistance measured as a short term modulus and creep ratio measured according to DIN-Certco ZP 14.3.1 (former DIN 54852-Z4) of 4.5 or below, more preferably 4.0 ore below, still more preferably 3.7 or below and most preferably 3.5 or below. The short term creep ratio is here defined as the creep modulus after 1 min divided by the creep modulus after 200 h.

Furthermore, the composition preferably has a creep modulus after 200 h of 450 MPa or more, more preferably of 500 MPa or more, still more preferably of 600 MPa or more, still more preferably of 700 MPa or more, and most preferably of 800 MPa or more.

The weldability of the composition measured as the ratio of the weld strength of a welded portion with respect to that of the full material is preferably higher than 0.5, more preferably higher than 0.7, still more preferably higher than 0.8, still more preferably higher than 0.9 and most preferably higher than 0.95.

The weldability of the composition can also be measured as the ratio of strain at break of the welded portion with respect to that of the full material. This ratio preferably is higher than 0.2, more preferably is higher than 0.3, still more preferably is higher than 0.5, still more preferably is higher than 0.7, still more preferably is higher than 0.8, and most preferably is higher than 0.9.

In the composition used for the pipe according to the invention preferably inorganic mineral filler (C) is present in an amount of at least 5 wt. %, more preferably at least 8 wt. %, still more preferably at least 10 wt. %, and most preferably at least 12 wt. %.

Furthermore, in the composition inorganic mineral filler (C) is present in an amount of at most 60 wt. %, more preferably of at most 50 wt. %. In particular as regards weld strength it is preferred that inorganic mineral filler (C) is present in an amount of at most 45 wt. %, more preferably of at most 30 wt. %, still more preferably at most 25 wt. %.

Filler (C) of the composition may comprise all inorganic mineral filler materials as known in the art. Filler (C) may also comprise a mixture of any such filler materials. Examples for such filler materials are oxides, hydroxides and carbonates of aluminium, magnesium, calcium and/or barium.

Preferably, filler (C) comprises an inorganic compound of a metal of groups 1 to 13, more preferred groups 1 to 3, still more preferred groups 1 and 2 and most preferred group 2, of the Periodic Table of Elements.

The numbering of chemical groups, as used herein, is in accordance with the IUPAC system in which the groups of the periodic system of the elements are numbered from 1 to 18.

Preferably, inorganic mineral filler (C) comprises a compound selected from carbonates, oxides and sulphates. Preferred examples of such compounds are calcium carbonate, talc, magnesium oxide, huntite Mg₃Ca(CO₃)₄, hydrated magnesium silicate and kaolin (“China clay”), with a particular preferred examples being calcium carbonate, magnesium oxide, hydrated magnesium silicate and kaolin (“China clay”).

Preferably, filler (C) comprises 50 wt % or more of calcium carbonate and further preferred is substantially made up completely of calcium carbonate.

Further preferred, the inorganic mineral filler has a weight average mean particle size of 25 micron or below, more preferably of 15 micron or below.

Preferably, only 2 wt % of the filler has a particle size of 30 microns or higher, more preferably of 25 micron or higher.

The purity of the filler preferably is 94% or higher, more preferably is 95% or higher and most preferably is 97% or higher.

In a preferred embodiment in which CaCO₃ is used as filler, preferably the particles have weight average mean particle size of 6 micron or below, more preferably of 4 micron or below.

In said embodiment, preferably only 2 wt % have a particle size of 8 micron or more, more preferably of 7 micron or more.

The inorganic mineral filler may comprise a filler which has been surface-treated with an organosilane, a polymer, a carboxylic acid or salt etc. to aid processing and provide better dispersion of the filler in the organic polymer. Such coatings usually do not make up more than 3 wt. % of the filler.

Preferably, the compositions according to the present invention contain less than 3 wt. % of organo-metallic salt or polymer coatings.

The shear thinning index (SHI) is the ratio of the viscosity of the polyethylene composition at different shear stresses. In the present invention, the shear stresses at 2.7 kPa and 210 kPa are used for calculating the SHI(_(2.7/210)) which may serve as a measure of the broadness of the molecular weight distribution.

Preferably, the composition has an shear thinning index SHI(_(2.7/210)) of 20 or more, more preferably of 30 or more.

Furthermore, the SHI(_(2.7/210)) of the composition is 150 or lower, more preferably is 120 or lower, still more preferably is 100 or lower, and most preferably is 70 or lower.

Preferably, the base resin has a density of 915 kg/m³ or more, more preferably of 920 kg/m³ or more, still more preferably of 930 kg/m³ or more, still more preferably of 940 kg/m³ or more, and most preferably of 950 kg/m³ or more.

It is furthermore preferred that the base resin has a density of 965 kg/m³ or less, more preferably of 960 kg/m³ or less, and most preferably 950 kg/m³ or less.

The composition preferably includes a copolymer of ethylene and one or more alpha-olefin comonomers, preferably of one or more C₄- to C₁₀-alpha olefin comonomers.

Preferably, the comonomer is selected from the group of 1-butene, 1-hexene, 4-methyl-1-pentene, 1-octene and 1-decene. Most preferably, the comonomer is 1-butene and/or 1-hexene.

Furthermore, it is preferred that the total amount of comonomer in the base resin is less than 2.0 mol %, more preferably less than 1 mol %, still more preferably less than 0.7 mol %, still more preferably less than 0.4 mol %, still more preferably less than 0.3 mol % and most preferably less than 0.2 mol %.

Fraction (A) of the polyethylene composition preferably has a density of 950 kg/m³ or higher, more preferably of 960 kg/m³ or higher, and most preferably of 968 kg/m³ or higher. Usually, the density of fraction (A) is 980 kg/m³ or below.

Preferably, fraction (A) has an MFR₂ of 20 to 2000 g/10 min, more preferably of 50 to 1500 g/10 min, and most preferably of 100 to 1200 g/10 min.

Furthermore, preferably fraction (B) is an ethylene copolymer, comprising preferably one or more of the above mentioned types of comonomers.

Fraction (B) of the composition preferably comprises at least 0.35 mol %, more preferably at least 0.55 mol %, and still more preferably at least 0.75 mol % of one or more of the above mentioned types of comonomers.

Fraction (B) of the polyethylene composition preferably has a density of 922 kg/m³ or higher, more preferably of 924 kg/m³ or higher, and most preferably of 927 kg/m³ or higher.

Furthermore, fraction (B) preferably has a density of 940 kg/m³ or below.

In the composition used for the pipe according to the invention, preferably the weight ratio of fractions (A):(B) in the base resin is 60:40 to 40:60, more preferably is 58:42 to 42:58, and most preferably is from 56:44 to 44:56.

In the polyethylene composition the ratio of MFR₂ of fraction (A) to MFR₅ of the base resin is preferably 10 or higher, more preferably 50 or higher, more preferably is from 100 to 10000.

Preferably, the base resin is consisting of fractions (A) and (B).

A pressure pipe made of the polymer composition preferably has a design stress rating of at least MRS 6.3, and more preferably MRS 8.0, still more preferably MRS 10.0, still more preferably MRS 11.2, still more preferably MRS 12.5, and most preferably MRS 14.0.

Where herein features of fractions (A) and/or (B) of the composition of the present invention are given, these values are generally valid for the cases in which they can be directly measured on the respective fraction, e.g. when the fraction is separately produced or produced in the first stage of a multistage process.

However, the base resin may also be and preferably is produced in a multistage process wherein e.g. fractions (A) and (B) are produced in subsequent stages. In such a case, the properties of the fractions produced in the second and third step (or further steps) of the multistage process can either be inferred from polymers, which are separately produced in a single stage by applying identical polymerisation conditions (e.g. identical temperature, partial pressures of the reactants/diluents, suspension medium, reaction time) with regard to the stage of the multistage process in which the fraction is produced, and by using a catalyst on which no previously produced polymer is present. Alternatively, the properties of the fractions produced in a higher stage of the multistage process may also be calculated, e.g. in accordance with B. Hagström, Conference on Polymer Processing (The Polymer Processing Society), Extended Abstracts and Final Programme, Gothenburg, Aug. 19 to 21, 1997, 4:13.

Thus, although not directly measurable on the multistage process products, the properties of the fractions produced in higher stages of such a multistage process can be determined by applying either or both of the above methods. The skilled person will be able to select the appropriate method.

The polyethylene composition according the invention preferably is produced so that at least one of fractions (A) and (B), preferably (B), is produced in a gas-phase reaction.

Further preferred, one of the fractions (A) and (B) of the polyethylene composition, preferably fraction (A), is produced in a slurry reaction, preferably in a loop reactor, and one of the fractions (A) and (B), preferably fraction (B), is produced in a gas-phase reaction.

Further, the polyethylene base resin preferably is an “in-situ”-blend. Such blends are preferably produced in a multistage process. However, an “in-situ”-blend may also be produced in one reaction stage by using two or more different kinds of catalyst.

A multistage process is defined to be a polymerisation process in which a polymer comprising two or more fractions is produced by producing each or at least two polymer fraction(s) in a separate reaction stage, usually with different reaction conditions in each stage, in the presence of the reaction product of the previous stage which comprises a polymerisation catalyst.

Accordingly, it is preferred that fraction (A) and (B) of the polyethylene composition are produced in different stages of a multistage process.

Preferably, the multistage process comprises at least one gas phase stage in which, preferably, fraction (B) is produced.

Further preferred, fraction (B) is produced in a subsequent stage in the presence of fraction (A) which has been produced in a previous stage.

It is previously known to produce multimodal, in particular bimodal, olefin polymers, such as multimodal polyethylene, in a multistage process comprising two or more reactors connected in series. As instance of this prior art, mention may be made of EP 517 868, which is hereby incorporated by way of reference in its entirety, including all its preferred embodiments as described therein, as a preferred multistage process for the production of the polyethylene composition according to the invention.

Preferably, the main polymerisation stages of the multistage process are such as described in EP 517 868, i.e. the production of fractions (A) and (B) is carried out as a combination of slurry polymerisation for fraction (A)/gas-phase polymerisation for fraction (B). The slurry polymerisation is preferably performed in a so-called loop reactor. Further preferred, the slurry polymerisation stage precedes the gas phase stage. The order of the stages may, however, also be reversed.

Optionally and advantageously, the main polymerisation stages may be preceded by a prepolymerisation, in which case up to 20% by weight, preferably 1 to 10% by weight, more preferably 1 to 5% by weight, of the total base resin is produced. The prepolymer is preferably an ethylene homopolymer (HDPE). At the prepolymerisation, preferably all of the catalyst is charged into a loop reactor and the prepolymerisation is performed as a slurry polymerisation. Such a prepolymerisation leads to less fine particles being produced in the following reactors and to a more homogeneous product being obtained in the end.

The polymerisation catalysts include coordination catalysts of a transition metal, such as Ziegler-Natta (ZN), metallocenes, non-metallocenes, Cr— catalysts etc. The catalyst may be supported, e.g. with conventional supports including silica, Al-containing supports and magnesium dichloride based supports. Preferably the catalyst is a ZN catalyst.

The resulting end product consists of an intimate mixture of the polymers from the two reactors, the different molecular-weight-distribution curves of these polymers together forming a molecular-weight-distribution curve having a broad maximum or two maxima, i.e. the end product is a bimodal polymer mixture.

It is preferred that the multimodal base resin of the polyethylene composition according to the invention is a bimodal polyethylene mixture consisting of fractions (A) and (B), optionally further comprising a small prepolymerisation fraction in the amount as described above. It is also preferred that this bimodal polymer mixture has been produced by polymerisation as described above under different polymerisation conditions in two or more polymerisation reactors connected in series. Owing to the flexibility with respect to reaction conditions thus obtained, it is most preferred that the polymerisation is carried out in a loop reactor/a gas-phase reactor combination.

Preferably, the polymerisation conditions in the preferred two-stage method are so chosen that the comparatively low-molecular polymer having no content of comonomer is produced in one stage, preferably the first stage, owing to a high content of chain-transfer agent (hydrogen gas), whereas the high-molecular polymer having a content of comonomer is produced in another stage, preferably the second stage. The order of these stages may, however, be reversed.

In the preferred embodiment of the polymerisation in a loop reactor followed by a gas-phase reactor, the polymerisation temperature in the loop reactor preferably is 85 to 115° C., more preferably is 90 to 105° C., and most preferably is 92 to 100° C., and the temperature in the gas-phase reactor preferably is 70 to 105° C., more preferably is 75 to 100° C., and most preferably is 82 to 97° C.

A chain-transfer agent, preferably hydrogen, is added as required to the reactors, and preferably 200 to 800 moles of H₂/kmoles of ethylene are added to the reactor, when the LMW fraction is produced in this reactor, and 0 to 50 moles of H₂/kmoles of ethylene are added to the gas phase reactor when this reactor is producing the HMW fraction.

The composition preferably if produced in a process comprising a compounding step, wherein the composition of the base resin, i.e. the blend, which is typically obtained as a base resin powder from the reactor, is extruded in an extruder and then pelletised to polymer pellets in a manner known in the art.

Preferably, in this extrusion step the filler and, optionally, other additives or other polymer components can be added to the composition in the amount as described above.

The extruder may be e.g. any conventionally used compounding or extruder unit, preferably is a co-rotating or counter-rotating twin screw extruder, or an internal mixer such as a Banburry type mixer or a single screw extruder such as a Buss co-kneader or a conventional single screw extruder. Static mixers such as Kenics, Koch, etc. can also be used in addition to the compounding or extruder units mentioned in order to improve the distribution of the filler in the polymer matrix.

Still further, the present invention relates the use of a polyethylene composition as described hereinbefore for the production of a pipe.

FIG. 1 shows the sample and the notch to be applied on the sample for the CTL test.

EXAMPLES

1. Definitions and Measurement Methods

a) Density

Density is measured according to ISO 1183/ISO 1872-2B.

b) Melt Flow Rate/Flow Rate Ratio

The melt flow rate (MFR) is determined according to ISO 1133 and is indicated in g/10 min. The MFR is an indication of the flowability, and hence the processability, of the polymer. The higher the melt flow rate, the lower the viscosity of the polymer. The MFR is determined at 190° C. and may be determined at different loadings such as 2.16 kg (MFR₂), 5 kg (MFR₅) or 21.6 kg (MFR₂₁).

The quantity FRR (flow rate ratio) is an indication of molecular weight distribution and denotes the ratio of flow rates at different loadings. Thus, FRR_(21/5) denotes the value of MFR₂₁/MFR₅.

c) Rheological Parameters

Rheological parameters such as Shear Thinning Index SHI and Viscosity are determined by using a rheometer, preferably a Anton Paar Physica MCR 300 Rheometer. The definition and measurement conditions are described in detail on page 8 line 29 to page 11, line 25 of WO 00/22040.

d) Rapid Crack Propagation

The rapid crack propagation (RCP) resistance of a pipe is determined according to a method called the S4 test (Small Scale Steady State), which has been developed at Imperial College, London, and which is described in ISO 13477:1997 (E).

According to the RCP-S4 test a pipe is tested, which has an axial length not below 7 pipe diameters. The outer diameter of the pipe is about 110 mm or greater and its wall thickness about 10 mm or greater. When determining the RCP properties of a pipe in connection with the present invention, the outer diameter and the wall thickness have been selected to be 110 mm and 10 mm, respectively. While the exterior of the pipe is at ambient pressure (atmospheric pressure), the pipe is pressurised internally, and the internal pressure in the pipe is kept constant at a pressure of 0.5 MPa positive pressure. The pipe and the equipment surrounding it are thermostatted to a predetermined temperature. A number of discs have been mounted on a shaft inside the pipe to prevent decompression during the tests. A knife projectile is shot, with well-defined forms, towards the pipe close to its one end in the so-called initiating zone in order to start a rapidly running axial crack. The initiating zone is provided with an abutment for avoiding unnecessary deformation of the pipe. The test equipment is adjusted in such a manner that crack initiation takes place in the material involved, and a number of tests are effected at varying temperatures. The axial crack length in the measuring zone, having a total length of 4.5 diameters, is measured for each test and is plotted against the set test temperature. If the crack length exceeds 4 diameters, the crack is assessed to propagate. If the pipe passes the test at a given temperature, the temperature is lowered successively until a temperature is reached, at which the pipe no longer passes the test, but the crack propagation exceeds 4 times the pipe diameter. The critical temperature (T_(crit)), i.e. the ductile brittle transition temperature as measured according to ISO 13477:1997 (E) is the lowest temperature at which the pipe passes the test. The lower the critical temperature the better, since it results in an extension of the applicability of the pipe.

e) Design Stress

The design stress rating is the circumferential stress a pipe is designed to withstand for 50 years without failure and is determined for different temperatures in terms of the Minimum Required Strength (MRS) according to ISO/TR 9080. Thus, MRS 6.3 means that the pipe is a pipe withstanding a hoop stress of 6.3 MPa gauge for 50 years at 20° C., MRS 8.0 means that the pipe withstands a hoop stress of 8 MPa gauge for 50 years at 20° C., etc.

f) Charpy Impact Strength

Charpy impact strength was determined according to ISO 179/1eA on V-notched samples at 23° C. (Charpy impact strength (23° C.)) and 0° C. (Charpy impact strength (0° C.))

g) Constant Tensile Load (CTL)

The CTL test is done with reference to ISO 6252-1992 (E), with the notch according to ASTM 1473, in the following way:

The CTL test is a test for accelerated slow crack growth where the acceleration is maintained by elevated temperature of 60° C. The testing is performed in a surface active solution and the incorporation of a notch both accelerates the time to failure and ensures a plain strain in the samples.

The stress in the samples was 5.0 MPa (actual stress in the notched region). The surfactant used in the test was IGEPAL CO-730 at a temperature of 60° C.

The samples are prepared by pressing a plaque with a total length of 125 to 130 mm and a width at its ends of 21±0.5 mm. The plaque then is milled into the correct dimensions in a fixture on two of the sides with a centre distance of both holders of 90 mm and a hole diameter of 10 mm. The central part of the plaque has a parallel length of 30±0.5 mm, a width of 9±0.5 mm, and a thickness of 6±0.5 mm.

A front notch of 2.5 mm depth is then cut into the sample with a razor blade fitted into a notching machine (PENT-NOTCHER, Norman Brown engineering), the notching speed is 0.2 mm/min. On the two remaining sides side grooves of 0.8 mm are cut which should be coplanar with the notch. After making the notches, the sample is conditioned in 2±1° C. and 50% relative humidity for at least 48 h. The samples are then mounted into a test chamber in which the active solution (10% water solution IGEPAL CO-730, chemical substance: nonyl phenyl polyethylene glycol ether) is kept. The samples are loaded with a dead weight and at the moment of breakage an automatic timer is shut off.

The sample and the notch to applied to the sample are shown in FIG. 1, in which:

A: total length 125 to 130 mm

B: width at ends 21±0.5 mm

C: centre distance between holders 90 mm

D: parallel length 30±0.5 mm

E: width of narrow parallel part 9±0.5 mm

F: hole diameter 10 mm

G: main notch 2.5±0.02 mm

H: side grooves 0.8 mm

I: thickness of plaque 6±0.2

i) Weld Strength

Weld strength was measured in accordance with DVS 2203, Teil 4 (tensile test), and is given as ratio of the strength of the welded material to the unwelded material.

As another measure of the properties and quality of the weld the strain at break is recorded during the measurement according to DVS 2203, Teil 4 (tensile test), given as a ratio of the strain at break of the welded to the unwelded material.

j) Creep Resistance

The short term creep ratio was measured in a four point bending mode according to DIN-Certco ZP 14.3.1 (former DIN 54852-Z4) at 1 min and 200 h. The long term creep ratio (pipe specimens) was determined according to ISO 9967.

k) Flexural Modulus

Flexural modulus was determined according to ISO 178.

2. Production of Polymer Compositions and Pipes

A base resin was produced in a multistage reaction comprising a first (pre)-polymerisation stage in slurry in a 50 dm³ loop reactor, followed by transferring the slurry to a 500 dm³ loop reactor wherein polymerisation was continued in slurry to produce the low molecular weight component, and a second polymerisation in a gas phase reactor in the presence of the product from the second loop reactor to produce the comonomer containing high molecular weight component. As comonomer, hexene-1 has been used.

As a catalyst, the supported catalyst as used in the examples of EP 1 137 707 was used.

The polymerisation conditions applied are listed in Table 1.

TABLE 1 Base resin Prepol. T/° C. 70 Prepol. H₂ feed 4.6 Prep. C₄/C₂ feed ratio 0 Loop T/° C. 95 Loop pressure/bar 60 Loop C₂ conc. 6.4 Loop H₂/C₂ 605 MFR₂/g/10 min 1000 Loop-Density homopol. GPR T/° C. 85 GPR C₂ conc. 9 H₂/C₂ 28 C₆/C₂ 17 Split 2/44/54 Density 954.2 kg/m³ Comonomer 0.72 wt. %

A composition was compounded/melt homogenized in a Buss Co-Kneader 100 MDK/E-11L/D. Polymer and additives (pellets and/or powder) were fed into the first mixer inlet of the Buss Co-Kneader which is a single screw extruder with a downstream discharge single screw extruder with a pelletizing unit cutting pellets in the molten stage and cooled via water. The mixer temperatures were set to 200 to 240° C., from first inlet to outlet, screw temperature to 210° C. and the discharge extruder to around 230° C. The mixer screw RPM was 170 to 190 rpm and the throughput 100 to 150 kg/h. The filler, as specified above, was fed into the molten polymer in the second mixer inlet downstream.

Composition 1 was produced by compounding the base resin with 40 wt. % of CaCO₃. The properties of Composition 1 compared to that of the base resin are given in Table 2.

The CaCO₃ used had a weight average mean particle size of 1.5 microns and only 2 wt % had a particle size of 8 micron or above, and a purity of 98.5% CaCO₃.

Pipes were produced by feeding the composition/base resin in pellet form into a conventional Cincinnati pipe extruder for extrusion with a line speed around 1 m/min into diameter 110 mm pipes with a wall thickness of 4 mm.

The extruders for producing the pipes can be standard pipe extruders, such as single screw extruders with an L/D of 20 to 40 or twin screw extruders or extruder cascades of homogenizing extruders (single screw or twin screw). Optionally, a melt pump and/or a static mixer can be used additionally between the extruder and the ring die head. Ring shaped dies with diameters ranging from approximately 16 to 2000 mm and even greater are possible.

After leaving the annular die, the pipe is taken off over a calibrating mandrel, usually accompanied by cooling of the pipe by air cooling and/or water cooling, optionally also with inner water cooling.

In the production of multilayer pipes conventional extruders are suitable. For example, the polyolefin layers may be manufactured with single screw extruders with an L/D of 20 to 40 or twin screw extruders or other types of extruders suitable for multilayer extrusion, as described for example in U.S. Pat. No. 5,387,386 and FI 83 184. Optionally, a melt pump and/or a static mixer can be used additionally between the extruder and the ring die head. Ring shaped dies with diameters ranging from approximately 20 to 2000 mm and even greater are possible. Advantageous die temperatures for discharging the melt are 180° C. to 240° C., preferably 200° C. to 240° C. After leaving the ring-shaped die, the polyolefin multilayer plastic pipes are taken off over a calibrating sleeve and cooled.

The multilayer pipe can also be manufactured in extrusion winding processes in diameters up to 3 to 4 meters or even larger.

The pipes may also be processed in corrugating devices in combination or close to the calibration step, for example for manufacturing of multilayer pipes of corrugated double/triple wall design with or without hollow sections or multilayer pipes with ribbed design.

Melt homogenisation and pipe production can also be made in one step without an intermediate solidification and pelletisation step, e.g. combined twin-screw extruder for both compounding and manufacturing of pipes.

TABLE 2 Base Resin Composition 1 (Comparative) eta (2.7 kPa) Pas 490 199 SHI (2.7/210) 44.3 41.5 eta (747 Pa) Pas 869 567 eta (368 Pa) Pas 1060 592 FRR_(21/5) 40.51 35.9 MFR₅ g/10 min 0.23 0.24 MFR₂₁ g/10 min 9.42 8.48 CTL(time to failure) h 53 52 flexural modulus MPa 2166 1402 Charpy impact kJ/m² 53.9 17.8 strength (23° C.) Charpy impact kJ/m² 32.8 14.2 strength (0° C.) Creep modulus after 1 min MPa 2918 1567 after 24 h MPa 1326 612 after 200 h MPa 907 433 Creep ratio 3.48 3.55 short term creep 3.22 3.61 ratio 

1. A pipe or a supplementary pipe article comprising a polyethylene composition comprising a base resin which comprises (A) a first ethylene homopolymer fraction, and (B) a second ethylene homo- or copolymer fraction, wherein fraction (A) has a lower average molecular weight than fraction (B), and the composition further comprises (C) an inorganic mineral filler, wherein inorganic mineral filler (C) is present in the composition in an amount of 1 to 70 wt. %.
 2. A pipe or a supplementary pipe article according to claim 1 wherein the composition has an MFR₅ of 0.1 to 2.0 g/10 min.
 3. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a flexural modulus determined according to ISO 178 of more than 1400 MPa.
 4. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a critical temperature in the EN 13477 test for determining the rapid crack propagation of −1° C. or less.
 5. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a slow crack propagation resistance of at least 50 h at 4.6 MPa hoop stress and 9.2 bar internal pressure at 80° C. measured according to EN
 13479. 6. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a time to failure in the CTL test of 25 h or more.
 7. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a weld ratio of the weld strength of a welded portion with respect to that of the full material of at least 0.5.
 8. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a weldability measured as the ratio of strain at break of the welded portion with respect to that of the full material of higher than 0.2.
 9. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a Charpy Impact Strength at 23° C. of more than 20 kJ/m².
 10. A pipe or a supplementary pipe article according to claim 1 wherein the composition has a Charpy Impact Strength at 0° C. of more than 10 kJ/m².
 11. A pipe or a supplementary pipe article according to claim 1 wherein inorganic mineral filler (C) is an inorganic compound of a metal of groups 1 to 13 of the Periodic System of the Elements or a mixture thereof.
 12. A pipe or a supplementary pipe article according to claim 1 wherein the base resin has a density of 915 kg/m³ or more.
 13. A pipe or a supplementary pipe article according to claim 1 wherein the composition includes a copolymer of ethylene and one or more alpha-olefin monomers.
 14. A pipe or a supplementary pipe article according to claim 13 wherein the amount of comonomer in the base resin is less than 2.0 mol %.
 15. A pipe or a supplementary pipe article according to claim 1 wherein fraction (B) is an ethylene copolymer comprising at least one alpha-olefin comonomer having at least 4 carbon atoms.
 16. A pipe or a supplementary pipe article according to claim 1 wherein fraction (A) has an MFR₂ of 20 to 2000 g/10 min.
 17. A pipe or a supplementary pipe article according to claim 1 wherein the weight ratio of fractions (A):(B) in the base resin is in the range of 60:40 to 40:60.
 18. A polyethylene composition adapted for the production of a pipe or a supplementary pipe article comprising a base resin which comprises (A) a first ethylene homopolymer fraction, and (B) a second ethylene homo- or copolymer fraction, wherein fraction (A) has a lower average molecular weight than fraction (B), and the composition further comprises (C) an inorganic mineral filler, wherein inorganic mineral filler (C) is present in the composition in an amount of 1 to 70 wt. %.
 19. A polyethylene pressure pipe comprising a base resin which comprises: (A) a first ethylene homopolymer fraction, and (B) a second ethylene homo- or copolymer fraction, wherein fraction (A) has a lower average molecular weight than fraction (B), and the composition further comprises (C) an inorganic mineral filler, wherein inorganic mineral filler (C) is present in the composition in an amount of 1 to 70 wt. %. 